How to improve wear resistance, anti fuzzing and pilling properties of fabrics?

1. Choose fibers that are not easy to pilling during yarn and fabric production.



2. Pretreatment and dyeing in jet dyeing machine with lubricant to prevent friction;

 
3. When dyeing cotton and polyester/cellulose blends with reactive dyes in jet dyeing machine, crystalline sodium sulfate can be used instead of common salt.

 
4. Proper heat setting is applied to polyester/cellulose and polyester/wool blended fabrics to make the yarn set and overfeed properly.

 
5, shearing at the same time brushing, can remove surface fibers and prominent fibers.

 
6, both sides are singled to remove surface fibers and protruding fibers.

 
7. For polyester and polyester/cellulose blended fabrics, partial alkali reduction of polyester components can reduce the strength of polyester, so the pellets can be easily removed.

 
8. Cellusof-L is used for cotton and polyester/cellulose blended fabrics, and suitable enzymes are used for polishing wool or polyester/wool blended fabrics.

 
9. Polyester/cellulose fibers, polyester/wool and cotton fabrics are treated with special additive Saraglow-CL in jet dyeing machine, and garments are washed in rotary cage to remove surface fibers.

 
10. Proper dosage should be used to avoid excessive softening and lubrication, otherwise the fibers will move to the surface and cause pilling.

 
11. Finishing with special finishing agents, such as Sarafeel-jy/Sarafeel-763, special organosilicon compound, can give fabric softness and improve pilling property through film forming; Sarasoft-MR organosilicon polymer finishing agent, with film forming property, can improve wear resistance; Garfinish-As has pilling resistance and abrasion resistance, can be added. In the traditional finishing solution formula.